- 1.2063/145Cr6/19422
- 1.2201/X165CrV12/19572
- 1.2885
- 1.2713
- 1.2343/X37CrMoV51/19552
- 1.1663
- 1.2550/19735/19733
- 1.2344/19554
- 1.2414
- 1.2842/19312
- 1.2365/19541
- 1.2379/19573
- 1.2080/19436
- 1.0535
- 1.0503/12050
- 1.3505/14109
- 1.3343/19830
- 1.3355
- 1.3207
- 1.7035/41Cr4/14140
- 1.7225/42CrMo4/15142
- 1.6511
- 30HGS
- 35HGS
- 1.7131/14220
- 1.7147
- 1.7262
- 18HGT
- 1.5920
- 1.8159/50CrV4/15260
- 50HS
- 1.1260/65G
- 1.8509/15340
- 1.0570/S355J2G3/11523
- 1.2085
- 1.2162
- 1.2210
- 1.2311/19520
- 1.2312
- 1.2316
- 1.2363
- 1.2367
- 1.2436
- 1.2738
- 1.2767
- 1.1231
- 1.1545
- 1.6582
- Abrazo 400/Nicrodur 400
- 4H13 / 1.4034/17029
- 1.4310
 |
 |
 |
 |
 |
Ložisková ocel
|
Druh ocele |
Chemické složení [%] |
|||||||||||
|
C |
Mn |
Si |
P |
S |
Cr |
Ni |
Mo |
W |
V |
Co |
Cu |
|
|
1.3505 |
0,95 - 1,1 |
0,25 -0,45 |
0,15 -0,35 |
MAX 0,027 |
MAX 0,027 |
1,3-1,65 |
MAX 0,3 |
- |
- |
- |
- |
MAX 0,30 |
|
Technologické obráběcí procesy |
Možnost použití |
Teplota, °C |
||
| Tváření |
Kování |
+ |
810-1150 |
|
|
Valcování |
+ |
770-1150 |
||
|
Tepelné zpracování |
Tepelné zušlechťování |
Kalení |
+ |
830-870 |
|
Popouštění |
+ |
150-170 |
||
|
Žíhání |
Změkčování |
+ |
780-810 |
|
| 1.3505 |
Hodnota |
|
Technologické obráběcí procesy |
|
| Tvrdost HB po žíhání s omezenou tvrdostí HB (HB) | <=235 |
| Tvrdost HB po měkkém žíhání HB (HB) | 170-207 |
| Tvrdost HB po tepelném vytvrzování po měkkém žíhání HB (HB) | 170-229 |
| Pevnost v tahu po měkkém žíhání Rm (MPa) | 570-720 |
| Pevnost v tahu po tepelném vytvrzování po měkkém žíhání Rm (MPa) | 590-780 |
|
Druhy ocele podle PN a W. a jejich ekvivalenty |
|||||||
|
PN |
W. NR |
DIN |
EN |
AISI |
RUSKO |
ČÍNA |
BÖHLER |
|
ŁH15 |
1.3505 |
100Cr6 |
100Cr6 |
52100 | SchCh15 | GCr15 |
- |
|
Sídlo: Akrostal Sp. z o.o. ul. Romana Maya 1 61-371 Poznań
|
Slezský překladní sklad: ul. Metalowa 4 43-100 Tychy |
Český překladní sklad: U cementárny 1183 703 00 Ostrava |
|
DIČ PL7822213458 Základní kapitál: 686 400 PLN
|
||